Reduced preheating type 1.デュエルビッツ 登録 - 0.5% Mo steel plates

1. Features

  • 400 N/mm2 class chromium-molybdenum alloy steel plates for boilers and pressure vessels for contributing to the reduction of welding costs and the improvement of the welding work environment during construction.
    • Preheating in welding construction can be greatly reduced.

2. Major corresponding standards

  • JIS G4109 (Chromium-molybdenum Alloy Steel Plates for Boilers and Pressure Vessels)
    SCMV3-1

3. Applications

  • The application of steel plates for various boilers and pressure vessels can be expected.

4. Typical characteristics

Classification Thickness
mm
Main chemical composition mass % Pcm2)
%
Base metal properties Weldability3)
C Si Mn Cr Mo Other
elements
SR
treatment
0.2%YS
N/mm2
TS
N/mm2
Prevention of weld cracking
Preheating temperature (°C) for preventing weld cracking
SR cracking ratio
%
Developed steel plate2) 50 0.07 0.64 0.54 1.26 0.48 Ni、Nb 0.22 690°C
x 8h
293 472 50 0
Conventional steel plate 50 0.12 0.64 0.57 1.32 0.51 - 0.27 325 495 125 0
Specification value1) 50 ≦0.17 0.50
to 0.80
0.40
to 0.65
1.00
to 1.50
0.45
to 0.65
- - - ≧235 410
to 590
- -
1) JIS G4109 SCMV3-1
2) Pcm(%)=C+Si/30+Mn/20+Cu/20+Ni/60+Cr/20+Mo/15+V/10+5B
3) JIS Z3158 Method of y-groove weld cracking test (the SR cracking ratio is measured after SR treatment at 690°C x 8 h)

Contacts

Plate Products (energy, plant, industrial machinery)

Request for Business or Catalog
Plate Products Sales Department
Iron & Steel Business デュエルビッツ 登録el, Ltd.
TEL: +81-3-5739-6154 (Tokyo)
TEL: +81-6-6206-6254 (Osaka)
Technical Matters
Plate Products Marketing & Technical Services
Iron & Steel Business デュエルビッツ 登録el, Ltd.
TEL: +81-3-5739-6261 (Tokyo)

Inquiry


* Please refer to the following link for products other than steel plates.

Page top