デュエルビッツ初回入金ボーナスowder for pressed powder magnetic cores with low steel loss and high shape flexibility

Features

1. Low steel loss and high efficiency
As a high heat-resistant insulated coating is formed on the デュエルビッツ初回入金ボーナスowder, high-temperature magnetic annealing of a compacted powder is possible.
In addition to alleviating compacting deformation due to annealing, steel loss is reduced by controlling デュエルビッツ初回入金ボーナスowder particle size and structure.
Additionally, by insulating the spaces between particles, eddy current loss at high frequency ranges can be reduced, making it possible to handle high-speed rotation and harmonics.
2. Support for three-dimensional design
As it is magnetically isotropic, three-dimensional circuit design can be supported.
Flexible circuit design is expected to enable lighter and more compact components.
3. Caters to a wide range of needs
We offer grades for die-lubricated compacting and internally-lubricated compacting, catering to diverse needs.
For die-lubricated compacting: High magnetic flux density and high strength
Internally-lubricated compacting: high productivity and complex shapes

ML-1000 and MH-2000 are for internally-lubricated compacting, while other types are for die-lubricated compacting.

Application	Steel grade name	Density (g/cm³)	Magnetic Flux Density B_10kA/m (T)	Maximum Relative Permeability	Coercive Force (A/m)	Core Loss^*1 (W/kg)	Transverse Rupture Strength (MPa)
Low frequency	ML35D	7.62	1.66	526	154	34	84
	ML28D	7.72	1.70	545	128	29	70
	ML-1000^*2	7.46	1.57	462	137	31	49
High frequency	MH23D	7.49	1.50	270	253	22	89
	MH20D	7.44	1.46	224	224	20	77
	MH-2000^*3	7.27	1.29	187	230	20	51

*1 Steel loss measurement conditions:
Low frequency applications　1T,400Hz, High frequency applications　100mT,10kHz

Specimen:φ45-φ33×5ｈ
Annealing: 600℃×30min (N₂GAS)
Die Lubrication Compacting:1176MPa,130℃
*2 Internal Lubrication Compacting:800MPa,80℃

*3 Internal Lubrication Compacting: 980MPa,RT